Surface and bulk cation distribution of the spinel system Zn_xMg_1-xFe₂O₄

Zn_xMg_1-xFe₂O₄ mixed oxide spinels (x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0) were prepared by conventional solid state reaction method. Bulk and surface characterization of these ferrites were carried out by different techniques. The ratios Zn/Fe and Mg/Fe determined by PIXE and AAS were nearly as expected from the synthesis mixture, i.e. following the substitution model. XRD shows only a spinel structure (fcc) with increasing lattice parameter as x increases from 0 to 1. The bulk ratios of tetrahedral to octahedral sites occupied by Fe cations measured by NGR are in good agreement with the theoretical bulk stoichiometry. LEIS results indicate a Mg substitution by Fe cations at the surface. Only octahedral sites are proposed at the surface. The transition from inverse to normal spinel was follow through NGR-spectra occurring at x = 0.4.