T1 - Ir-Sn-Sb-O electrocatalyst for oxygen evolution reaction
T2 - Physicochemical characterization and performance in water electrolysis single cell with solid polymer electrolyte
AU - Pérez-Viramontes, Nicté J.
AU - Collins-Martínez, Virginia H.
AU - Escalante-García, Ismailia L.
AU - Flores-Hernández, José R.
AU - Galván-Valencia, Marisol
AU - Durón-Torres, Sergio M.
N1 - Publisher Copyright:
© 2020 by the authors. Licensee MDPI, Basel, Switzerland.
PY - 2020/5
Y1 - 2020/5
N2 - Mixed oxide Ir-Sn-Sb-O electrocatalyst was synthesized using thermal decomposition from chloride precursors in ethanol. Our previous results showed that Ir-Sn-Sb-O possesses electrocatalytic activity for an oxygen evolution reaction (OER) in acidic media. In the present work, the physicochemical characterization and performance of Ir-Sn-Sb-O in an electrolysis cell are reported. IrO2 supported on antimony doped tin oxide (ATO) was also considered in this study as a reference catalyst. Scanning electron microscopy (SEM) images indicated that Ir-Sn-Sb-O has a mixed morphology with nanometric size. Energy dispersive X-ray spectroscopy (EDS) showed a heterogeneous atomic distribution. Transmission electron microscopy (TEM) analysis resulted in particle sizes of IrO2 and ATO between 3 to >10 nm, while the Ir-Sn-Sb-O catalyst presented non-uniform particle sizes from 3 to 50 nm. X-ray diffraction (XRD) measurements indicated that synthesized mixed oxide consists of IrO2, IrOx, doped SnO2 phases and metallic Ir. The Ir-Sn-Sb-O mixed composition was corroborated by temperature programmed reduction (TPR) measurements. The performance of Ir-Sn-Sb-O in a single cell electrolyser showed better results for hydrogen production than IrO2 /ATO using a mechanical mixture. Ir-Sn-Sb-O demonstrated an onset potential for water electrolysis close to 1.45 V on Ir-Sn-Sb-O and a current density near to 260 mA mg−1 at 1.8 V. The results suggest that the mixed oxide Ir-Sn-Sb-O has favorable properties for further applications in water electrolysers.
AB - Mixed oxide Ir-Sn-Sb-O electrocatalyst was synthesized using thermal decomposition from chloride precursors in ethanol. Our previous results showed that Ir-Sn-Sb-O possesses electrocatalytic activity for an oxygen evolution reaction (OER) in acidic media. In the present work, the physicochemical characterization and performance of Ir-Sn-Sb-O in an electrolysis cell are reported. IrO2 supported on antimony doped tin oxide (ATO) was also considered in this study as a reference catalyst. Scanning electron microscopy (SEM) images indicated that Ir-Sn-Sb-O has a mixed morphology with nanometric size. Energy dispersive X-ray spectroscopy (EDS) showed a heterogeneous atomic distribution. Transmission electron microscopy (TEM) analysis resulted in particle sizes of IrO2 and ATO between 3 to >10 nm, while the Ir-Sn-Sb-O catalyst presented non-uniform particle sizes from 3 to 50 nm. X-ray diffraction (XRD) measurements indicated that synthesized mixed oxide consists of IrO2, IrOx, doped SnO2 phases and metallic Ir. The Ir-Sn-Sb-O mixed composition was corroborated by temperature programmed reduction (TPR) measurements. The performance of Ir-Sn-Sb-O in a single cell electrolyser showed better results for hydrogen production than IrO2 /ATO using a mechanical mixture. Ir-Sn-Sb-O demonstrated an onset potential for water electrolysis close to 1.45 V on Ir-Sn-Sb-O and a current density near to 260 mA mg−1 at 1.8 V. The results suggest that the mixed oxide Ir-Sn-Sb-O has favorable properties for further applications in water electrolysers.
KW - Ir-Sn-Sb-O
KW - OER electrocatalyst
KW - Solid polymer electrolyte water electrolyser
UR - http://www.scopus.com/inward/record.url?scp=85084808650&partnerID=8YFLogxK
U2 - 10.3390/catal10050524
DO - 10.3390/catal10050524
M3 - Artículo
AN - SCOPUS:85084808650
SN - 2073-4344
VL - 10
JO - Catalysts
JF - Catalysts
IS - 5
M1 - 524
ER -