Abstract
The effect of WOx on the microstructure, Lewis acidity and catalytic conversion of Pt/Al2O3 catalysts was studied. High surface areas were obtained at low W concentration and the WOx species decreased the Al2O3 surface area and Lewis acid sites. WOx species in tetrahedral coordination were found. Multiple layers of close-packed spheres forming pores were seen on the Al2O3. The addition of WOx produced semi-cubic particles and the spheres disappeared. At low W concentrations (0.5-2 wt%W) dehydrociclization and isomerization selectivities were higher than the hydrocracking selectivity. On the contrary high hydrocracking selectivity was found for samples with high W concentration (4-22 wt%W).
Original language | English |
---|---|
Pages (from-to) | 450-452 |
Number of pages | 3 |
Journal | Journal of Alloys and Compounds |
Volume | 483 |
Issue number | 1-2 |
DOIs | |
State | Published - 26 Aug 2009 |
Keywords
- Nanostructures
- Scanning and transmission electron microscopy
- Sol-gel synthesis
- Surfaces and interfaces