Abstract
Results of studying the thermoluminescent response of undoped ZrO2 + PTFE pellets irradiated with 90Sr/90Y beta particles are presented. Previously, TL characteristics of ZrO2 films doped with rare earths were studied. Phosphor powder was obtained by evaporating a solution of zirconium nitrate in ethanol. In order to stabilise the traps in ZrO2 this phosphor was submitted to different thermal treatments. Optimal thermal treatment consisted in heating at 1100°C for 24 h. With this powder, pressing at room temperature a mixture (2:1) of ZrO2 and polytetrafluoroethylene (PTFE), pellets of 5 mm diameter and 0.8 mm thickness were made. The glow curve of ZrO2+PTFE pellets exhibited two peaks at 200 and 250°C; its TL response as a function of beta particles dose was linear in the range from 2 to 60 Gy. Repeatability over 10 cycles was 1.8%. Fading at room temperature was 3.8% per month.
Original language | English |
---|---|
Pages (from-to) | 317-319 |
Number of pages | 3 |
Journal | Radiation Protection Dosimetry |
Volume | 100 |
Issue number | 1-4 |
DOIs | |
State | Published - 2002 |
Externally published | Yes |