TY - JOUR
T1 - Low-temperature processed ZnO and CdS photodetectors deposited by pulsed laser deposition
AU - Hernandez-Como, N.
AU - Moreno, S.
AU - Mejia, I.
AU - Quevedo-Lopez, M. A.
PY - 2014/8/1
Y1 - 2014/8/1
N2 - UV-VIS photodetectors using an interdigital configuration, with zinc oxide (ZnO) and cadmium sulfide (CdS) semiconductors deposited by pulsed laser deposition, were fabricated with a maximum processing temperature of 100 °C. Without any further post-growth annealing, the photodetectors are compatible with flexible and transparent substrates. Aluminum (Al) and indium tin oxide (ITO) were investigated as contacts. Focusing on underwater communications, the impact of metal contact (ITO versus Al) was investigated to determine the maximum responsivity using a laser with a 405 nm wavelength. As expected, the responsivity increases for reduced metal finger separation. This is a consequence of reduced carrier transit time for shorter finger separation. For ITO, the highest responsivities for both films (ZnO and CdS) were ∼3 A W-1 at 5 V. On the other hand, for Al contacts, the maximum responsivities at 5 V were ∼0.1 A W-1 and 0.7 A W-1 for CdS and ZnO, respectively.
AB - UV-VIS photodetectors using an interdigital configuration, with zinc oxide (ZnO) and cadmium sulfide (CdS) semiconductors deposited by pulsed laser deposition, were fabricated with a maximum processing temperature of 100 °C. Without any further post-growth annealing, the photodetectors are compatible with flexible and transparent substrates. Aluminum (Al) and indium tin oxide (ITO) were investigated as contacts. Focusing on underwater communications, the impact of metal contact (ITO versus Al) was investigated to determine the maximum responsivity using a laser with a 405 nm wavelength. As expected, the responsivity increases for reduced metal finger separation. This is a consequence of reduced carrier transit time for shorter finger separation. For ITO, the highest responsivities for both films (ZnO and CdS) were ∼3 A W-1 at 5 V. On the other hand, for Al contacts, the maximum responsivities at 5 V were ∼0.1 A W-1 and 0.7 A W-1 for CdS and ZnO, respectively.
KW - UV photodetectors
KW - cadmium sulfide
KW - pulsed laser deposition
KW - zinc oxide
UR - http://www.scopus.com/inward/record.url?scp=84904643660&partnerID=8YFLogxK
U2 - 10.1088/0268-1242/29/8/085008
DO - 10.1088/0268-1242/29/8/085008
M3 - Artículo
SN - 0268-1242
VL - 29
JO - Semiconductor Science and Technology
JF - Semiconductor Science and Technology
IS - 8
M1 - 085008
ER -