T1 - Coarsening of β′ precipitates in an isothermally aged Fe 75-Ni10-Al15 alloy
AU - Soriano-Vargas, Orlando
AU - Dorantes-Rosales, Hector J.
AU - Saucedo-Muñoz, Maribel L.
AU - Lopez-Hirata, Victor M.
AU - Lezama-Alvarez, Susana
AU - Avila-Davila, Erika O.
PY - 2011
Y1 - 2011
N2 - The coarsening process of the β′ precipitates was studied in an isothermally aged Fe75-Ni10-Al15 alloy. The aging treatments at 750, 850, and 920°C caused the precipitation of the β′phase with the B2 type crystalline structure in a bcc ferritic matrix phase. As the aging progressed, the initial rounded shape changed to cuboids aligned in the 〈100〉 directions of the ferritic matrix, and finally to rectangular plates also aligned in the same direction. The coarsening process of the β′phase was faster as the aging temperature increased. Nevertheless, the highest hardness and slowest overaging process took place during the aging at 920°C. This increase in hardness seems to be associated with the more rapid formation of the cuboid precipitates aligned in the 〈100〉 direction of the ferritic matrix.
AB - The coarsening process of the β′ precipitates was studied in an isothermally aged Fe75-Ni10-Al15 alloy. The aging treatments at 750, 850, and 920°C caused the precipitation of the β′phase with the B2 type crystalline structure in a bcc ferritic matrix phase. As the aging progressed, the initial rounded shape changed to cuboids aligned in the 〈100〉 directions of the ferritic matrix, and finally to rectangular plates also aligned in the same direction. The coarsening process of the β′phase was faster as the aging temperature increased. Nevertheless, the highest hardness and slowest overaging process took place during the aging at 920°C. This increase in hardness seems to be associated with the more rapid formation of the cuboid precipitates aligned in the 〈100〉 direction of the ferritic matrix.
KW - Coarsening mechanism
KW - Fe-Ni-Al alloys
KW - β′ phase precipitation
UR - http://www.scopus.com/inward/record.url?scp=79960634813&partnerID=8YFLogxK
M3 - Contribución a la conferencia
AN - SCOPUS:79960634813
SN - 9781118029473
T3 - TMS Annual Meeting
SP - 569
EP - 576
BT - TMS 2011 - 140th Annual Meeting and Exhibition, Supplemental Proceedings
T2 - TMS 2011 - 140th Annual Meeting and Exhibition
Y2 - 27 February 2011 through 3 March 2011
ER -