TiO2/C composite as a support for Pd-nanoparticles toward the electrocatalytic oxidation of methanol in alkaline media

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

37 Citas (Scopus)

Resumen

The electro-oxidation of methanol was studied in alkaline solution on Pd nanoparticles supported on carbon black (XC-72R, C) and TiO2/C composite. The materials were prepared via organic colloid route at 170 C with 5 wt% of Pd. X-ray diffraction (XRD), PdO monolayer reduction (PdOred) and CO-stripping was employed to characterize both structure and electrochemical properties. According to this, the lattice parameter decreases from 0.3991 to 0.3905 nm due to a possible formation of Pd-Ti alloy. This modification is linked with the electrochemical active surface area (ECSA) decreasing from 22 to 18 m2 g-1. On the other hand, studies as a function of temperature and alcohol concentration indicated that the current for methanol electro-oxidation is higher and more stable at Pd/TiO2-C, with Ea = 44.042 kJ mol-1. Then, it is highly possible that at Pd/TiO2-C, the OH-/OH ads couple is adsorbed at the TiO2 sites, increasing the kinetic of methanol oxidation reaction at the catalyst surface.

Idioma originalInglés
Páginas (desde-hasta)164-170
Número de páginas7
PublicaciónElectrochimica Acta
Volumen112
DOI
EstadoPublicada - 2013
Publicado de forma externa

Huella

Profundice en los temas de investigación de 'TiO2/C composite as a support for Pd-nanoparticles toward the electrocatalytic oxidation of methanol in alkaline media'. En conjunto forman una huella única.

Citar esto