TY - JOUR
T1 - Synthesis and characterization of Y2O3:Pr3+ phosphor powders by simple solvent evaporation
AU - Alarcón-Flores, G.
AU - García-Hipolito, M.
AU - Aguilar-Frutis, M.
AU - Zaleta-Alejandre, E.
AU - Chacón, Cecilia
AU - Ramos-Brito, F.
AU - Carmona-Téllez, S.
AU - Guzmán-Mendoza, J.
AU - Falcony, C.
N1 - Publisher Copyright:
© 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
PY - 2015/1
Y1 - 2015/1
N2 - The synthesis of trivalent praseodymium doped yttrium oxide powders (Y2O3:Pr3+) by the solvent evaporation method as well as their structural and luminescent (cathodoluminescence and photoluminescence) properties are reported as a function of the concentration of the reagents and annealing temperatures in the 400 to 1100 °C range. These powders become polycrystalline in a cubic Y2O3 structure at temperatures above 600 °C. An increase in the diffraction peaks intensity was observed as the temperature is increased. Transmission electron microscopy analysis showed irregular needle like crystallites and the characteristic electron diffraction rings for polycrystalline powders on samples annealing above 600 °C. Scanning electron microscopy showed that these crystallites clump into larger particles of irregular shape. Luminescence spectra show the characteristic peaks at 620 and 630 nm due to 1D2 to 3H4 transitions in Pr3+ ions in the Y2O3 host.
AB - The synthesis of trivalent praseodymium doped yttrium oxide powders (Y2O3:Pr3+) by the solvent evaporation method as well as their structural and luminescent (cathodoluminescence and photoluminescence) properties are reported as a function of the concentration of the reagents and annealing temperatures in the 400 to 1100 °C range. These powders become polycrystalline in a cubic Y2O3 structure at temperatures above 600 °C. An increase in the diffraction peaks intensity was observed as the temperature is increased. Transmission electron microscopy analysis showed irregular needle like crystallites and the characteristic electron diffraction rings for polycrystalline powders on samples annealing above 600 °C. Scanning electron microscopy showed that these crystallites clump into larger particles of irregular shape. Luminescence spectra show the characteristic peaks at 620 and 630 nm due to 1D2 to 3H4 transitions in Pr3+ ions in the Y2O3 host.
KW - Photoluminescence spectroscopy
KW - Polycrystalline powders
KW - Trivalent praseodymium
KW - Yttrium oxide
UR - http://www.scopus.com/inward/record.url?scp=84922789737&partnerID=8YFLogxK
U2 - 10.1016/j.ceramint.2014.08.133
DO - 10.1016/j.ceramint.2014.08.133
M3 - Artículo
SN - 0272-8842
VL - 41
SP - 743
EP - 748
JO - Ceramics International
JF - Ceramics International
IS - 1
ER -