Synthesis and characterization of bismuth alkaline titanate powders

A. M. Torres-Huerta, M. A. Domínguez-Crespo, M. A. Hernández-Pérez, D. S. García-Zaleta, S. B. Brachetti-Sibaja

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

Resumen

In this work, samples of bismuth alkaline titanate, (K0.5Na 0.5)(2-x/2)Bi(x/6)TiO3, (x = 0.05-0.75) have been prepared by conventional ceramic technique and molten salts. Metal oxides or carbonates powders were used as starting raw materials. The crystalline phase of the synthesized powders was identified by the X-ray diffraction (XRD) and particle morphology was characterized by scanning electron microscopy (SEM). Solid state reaction method was unsuccessful to obtain pellets. From XRD results, a rhombohedral structure was detected and the parameter lattice were estimated to be a = 5.5478 and α = 59.48°. These parameters were used to refine the structure by Rietveld analysis. SEM results showed several morphologies. Apparently, bismuth is promoting the grain growth whose sizes vary from 30 nm to 180 nm It is expected that these materials can be utilized in practical applications as substitutes for lead zirconatetitanate (PZT)-based ceramics.

Idioma originalInglés
Páginas (desde-hasta)S375-S379
PublicaciónJournal of Alloys and Compounds
Volumen509
N.ºSUPPL. 1
DOI
EstadoPublicada - 14 jul. 2011

Huella

Profundice en los temas de investigación de 'Synthesis and characterization of bismuth alkaline titanate powders'. En conjunto forman una huella única.

Citar esto