Resumen
The Ca5Bi3 intermetallic compound was synthesized by milling Ca and Bi. Ca5Bi3 was obtained using a high-energy mill. A stoichiometric mixture of elemental powders was formed after three hours of milling. Next, the grade reagents, calcium and bismuth, were melted by heating at 1613 K for 12 h in sealed steel ampoules to prevent oxidation. The intermetallic compound was compacted using a hot isostatic press with 300 MPa and sintered at 673 K. The compound was characterized by chemical analysis, X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The product contains 1.68% Ca, 94.56% Bi and 5.43% O after milling, melting and press-sintering.
Título traducido de la contribución | Síntesis Y Caracterización Del Sistema Ca5Bi3 Obtenido Por Aleado Mecánico Y Sinterización Y Su Transformación De Fase Por Microscopía Electrónica De Barrido |
---|---|
Idioma original | Inglés |
Páginas (desde-hasta) | 146-151 |
Número de páginas | 6 |
Publicación | Acta Microscopica |
Volumen | 24 |
N.º | 2 |
Estado | Publicada - 2015 |
Publicado de forma externa | Sí |