Growth Kinetics of CoB-Co <inf>2</inf> B Layers Using the Powder-Pack Boriding Process Assisted by a Direct Current Field

I. Campos-Silva, O. Franco-Raudales, J. A. Meda-Campaña, F. P. Espino-Cortés, J. C. Acosta-Pavón

Research output: Contribution to journalArticlepeer-review

1 Scopus citations

Abstract

© 2019 Walter de Gruyter GmbH, Berlin/Boston 2019. New results about the growth kinetics of CoB-Co 2 B layers developed at the surface of CoCrMo alloy using the powder-pack boriding process assisted by a direct current field (PBDCF) were estimated in this work. The PBDCF was conducted at temperatures of 1048-1148 K with different exposure times for each temperature, whereas the growth kinetics of the cobalt boride layers was modelled using a system of two differential equations. In addition, indentation properties such as hardness, Young's modulus and residual stresses were estimated along the depth of the borided CoCrMo surface. The growth kinetics of the cobalt boride layers developed by PBDCF indicated that thicker boride layers were formed on the material's surface which was in contact to the current field at the anode, in contrast to the surface exposed at the cathode. The kinetics of cobalt boride layers were compared with those obtained by conventional powder-pack boriding process.
Original languageAmerican English
Pages (from-to)158-167
Number of pages10
JournalHigh Temperature Materials and Processes
DOIs
StatePublished - 1 Jan 2019

Fingerprint Dive into the research topics of 'Growth Kinetics of CoB-Co <inf>2</inf> B Layers Using the Powder-Pack Boriding Process Assisted by a Direct Current Field'. Together they form a unique fingerprint.

Cite this